| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | 343 - 387 |
| Density | g mL-1 | 1.33 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 4.5 - 5.5 |
| Heat Deflection Temperature, 0.5 MPa | °C | - |
| Heat Deflection Temperature, 1.8 MPa | °C | 152 - 172 |
| Thermal Conductivity | W / mK | 0.29 |
| Rockwell Hardness, M Scale | n/a | M100 - M124 |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 100 - 115 |
| Tensile Strength, Break at 23 C | MPa | - |
| Elongation, Yield | % | - |
| Elongation, Break | % | 15 - 45 |
| Tensile Modulus at 23 C | MPa | 3725 |
| Flexural Strength, Yield | MPa | 165 - 185 |
| Flexural Modulus | MPa | 4065 - 4275 |
| Compressive Strength | MPa | 120 |
| Izod Notched | kJ / m2 | 4.4 - 7.6 |
| Izod Unnotched | kJ / m2 | no break |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | 2.5 - 3.3 | |
| Dielectric Constant @ 1 MHz | n/a | 2.8 - 3.3 | |
| Dissipation Factor @ 1 MHz | n/a | 0.001 - 0.005 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 370 - 400 | |
| Mold Shrinkage | % | 1.0 - 1.3 | |
| Continuous Service Temperature | °C | 220 -250 | |
| Water Absorption, 24 hr. Immersion | % | 0.05 - 0.2 |